TOA SUPER MATEX RED OXIDE PRIMER

TOA SUPER MATEX RED OXIDE PRIMER : It is a primer based on red iron as anticorrosive pigment and a special alkyd as vechiale agent. It is characterized with quick drying, good flow and strong adhesion for metal substrate.

• Rust preventive.
  
• Easy to paint, Quick drying.
  
• Reinforcee adhesion to top coating.
  
• Durable and fungus resistance.
  
• Low  odor, safe for users and environment.
  

FEATURES

It is primer based on red oxide as anticorrosive pigment and a special alkyd as vechicle agent. It is characterized with quick drying, good flow and strong adhesion for metal substrate Its seneral purpose is for prime coating on gerenal construction steel such as fabricated. such as fabricated steel, machineries, iron, gates, grills for the windows, ect.

 APPLICATION SYSTEM 
Surface Preparation

• Old surface ( Steel )

• • Polishing the paint film peeling out and clean the dust, rust and grease-free 

• Old surface ( Wood )

• • Polishing the paint film peeling out and clean the dust and grease-free
• New surface

• • Steel substrate must be prepared ,free from rust,millscale,dirt,loose particles,and waxy contaminate. 

• • Wood substrate must be prepared ,free from dirt,loose particles,and waxy contaminate. 

Coating system

• Primer
  • Steel

• • • Supertech Red Oxide Primer 1 – 2 coat. (40 µ per coat)

• • Alloy

• • • Apply 1 coat Toa Wash Primer for galvanized steel and aluminium alloy surface (10 µ per coat)

• • • Supertech Red Oxide Primer 1 – 2 coat. (40 µ per coat)
• Topcoat

• • Apply Supertech Enamel gloss 2 coat (30 µ per coat)

Recommendation

• The temperature of the substrate should be minimum 10 ํC and at least 3 ํC above the dew point of  the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.